White 80um 170um PES Hot Melt Powder Used In Textiles And Garments

Contact me for free samples and coupons.
Whatsapp:0086 18588475571
Wechat: 0086 18588475571
Skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xColor | White | Composition | Copolyester |
---|---|---|---|
Appearance | White Powder | Melt Point(DSC) | 105-115 ℃ |
Melt Flow Index | 30±7 G/10min | Washable Property | 40℃ Excellent 60℃ Good 90℃Ordinary |
Powder Size Range | 0-80μm; 80-170μm;150-250μm | Density | 1.20±0.02 G/cm³ |
Packaging | 20KG In One PE Bag+Brown Paper | Product Type | Heat Transfer Adhesive Powder |
High Light | PES Hot Melt Powder,170um Hot Melt Powder,170um Hot Melt Glue Powder |
White 80μm 170μm PES Hot Melt Powder Used In Textiles And Garments
Heat Transfer Adhesive Powder Product model: ES203
Description: copolyester thermoplastic powder hot melt adhesive.
Application: DS203 is used in textiles and garments, automotive interiors, filters, shoe materials, heat transfer pastes, flocking pastes and bronzing pastes.
Physical Characteristics:
Property | Criterion |
Appearance | White powder |
Composition | Copolyester |
Density ASTM D-792 | 1.20±0.02 g/cm³ |
Melt Point DSC | 105-115 ℃ |
Melt Index ASTM D-1238 | 30±7 g/10min |
Powder size range | 0-80 um |
80-170 um | |
150-250 um |
Technical Parameters:
Bonding parameters (for reference only) | Temperature | 125-140℃ |
Press | 1.5-3.0kg/cm2 | |
Time | 10-18S | |
Washing Resistance | 40℃ | Excellent |
60℃ | Good | |
90℃ | / |
Packaging and Storage Conditions:
Packaging | 20KG in one PE bag+Brown paper bag |
Storage Conditions | Stored in dry unopened packaging at room temperature for 12 months. High temperature and pressure will cause agglomeration. The trays cannot be double-pressed. |
1. Bonding temperature and pressure and time relate to the bonding strength of the film to the material. The bonding temperature must be close to the temperature set by the machine, the pressure must be uniform, and the mold and press rolls must be flat.