Washable White PA Polyamide Powder Hot Melt For Heat Transfer

Contact me for free samples and coupons.
Whatsapp:0086 18588475571
Wechat: 0086 18588475571
Skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xKeyword | PA Hot Melt Adhesive Powder | Density ASTM D-792 | 1.10±0.02 G/cm³ |
---|---|---|---|
Melt Point DSC | 120-130 ℃ | Melt Index ASTM D-1238 | 25±5 G/10min |
Powder Size Range | 0-80μm,80-170 μm,100-400 μm | Temperature | 130-160℃ |
Washing Resistance | 90℃ | Packaging | 20KG |
High Light | PA Polyamide Powder,ROHS Polyamide Powder,Polyamide Hot Melt Powder |
Washable White PA Polyamide Powder Hot Melt For Heat Transfer
PA Hot Melt Adhesive Powder Description
The product is thermoplastic copolyamide powder hot melt adhesive. This product has excellent adhesion excellent resistance to washing and dry cleaning for textile category.
PA Hot Melt Adhesive Powder Applications
ES211 is used in textiles and garments automotive interiors ,filters, shoe materials, heat transfer pastes, flocking pastes and bronzing pastes.
PA Hot Melt Adhesive Powder Physical Characteristics:
Property | Criterion |
Appearance | White powder |
Composition | C0-PA |
Density ASTM D-792 | 1.10±0.02 g/cm³ |
Melt Point DSC | 120-130 ℃ |
Melt Index ASTM D-1238 | 25±5 g/10min |
Powder size range | 0-80 μm |
0-120μm | |
0-160 μm | |
80-170 μm | |
80-300 μm | |
100-400 μm |
Technical Parameters:
Bonding Parameters ( reference only) |
Temperature | 130-160℃ |
Press | 1.5-3.0 kg/cm2 | |
Time | 10-18 S | |
Washing Resistance | 40℃ | Excellent |
60℃ | Great | |
90℃ | Good |
PA Hot Melt Adhesive Powder Packaging and Storage Conditions:
Packaging | 20KG in one PE bag |
Storage Conditions | Stored in dry unopened packaging at room temperature for 12 months. High temperature and pressure will cause agglomeration. The trays cannot be double-pressed. |
Legal statement: The above data is based on the average of Tunsing Lab's multiple experiments with the general issues and recommendations of the product and application. It can not be construed as proof of the warranty for the product characteristics or the suitability of the particular area. Using units should be selected according to their own conditions and selective test. The user shall determine the suitability and fitness of the product for its intended use before using, and to take risks and possible problems in each manufacturing process of test and use. The seller and the manufacturer shall not bear any liability for any direct injury, loss, damage or misuse.