Introduces DS001TS Copolyester Hot Melt Adhesive Film: Elevating Bonding Efficiency in Apparel and Footwear Manufacturin

As the global manufacturing sector continuously demands high-efficiency, reliable, and versatile bonding materials, Shenzhen Tunsing Plastic Products Co., Ltd. has officially launched its high-performance thermoplastic film-like adhesive: the DS001TS Copolyester Hot Melt Adhesive Film. Engineered to support repeatable heating and plasticization for seamless bonding, this product is setting a new benchmark for structural adhesion across multiple consumer and industrial sectors.

The DS001TS is a copolyester-based adhesive film designed with a Milky white, semi-transparent appearance and backed by high-quality Glassine release paper. According to its official Technical Data Sheet (TDS), the film boasts exceptional physical characteristics that guarantee consistent production outcomes:

• Proportion: $1.15pm0.02text{g/cm}^3$

• Melt Flow Index (MI): $32pm15text{cm}^3/10text{mins}$ (Tested under ASTM D1238-04)

• Melting Point (DSC): 80°C - 105°C (Tested under ISO11357)

• Activation Temperature: 116°C - 150°C (Tunsing Standard)

DS001TS exhibits outstanding adhesion strength on textiles, PVC, and PC substrates. This makes it an ideal choice for bonding clothing, footwear, accessories, reflective materials, handbags, luggage, embroidery, and handicrafts. Furthermore, end-products bonded with DS001TS possess high durability, as the adhesive is fully dry-cleanable and can withstand machine washing at 40°C.

To seamlessly integrate into diverse automated manufacturing lines, Tunsing offers DS001TS in a wide variety of dimensions:

• Conventional Thicknesses: Available in 0.05mm, 0.08mm, 0.10mm, 0.12mm, and 0.15mm.

• Width Range: Fully customizable from 5mm up to 1580mm (with a conventional width of 500mm).

• Finished Product Packaging: Supplied in convenient 500mm * 100yard/roll formats.

For optimal manufacturing results, the technical team recommends the following basic lamination parameters:

1. First Lamination: Mechanical mold temperature of 130°C - 160°C, dwell time of 5 - 15 seconds, and uniform pressure of 0.3 - 0.6MPa.

2. Second Lamination: Mechanical mold temperature of 130°C - 170°C, dwell time of 8 - 25 seconds, and uniform pressure of 0.3 - 0.6MPa.

Tunsing reminds manufacturers that because bonding conditions vary depending on the machinery and substrates used, ideal custom parameters should be established via pre-production verification.